點擊圖片查看大圖| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 基本性能 | 比重 | ASTM D792 | 1.41 | g/cm3 | |
| 熔體質量流動速率 | ASTM D1238 | 16 | g/10 min | ||
| 成型收縮率 | flow | ASTM D955 | 2.0 | % | |
| 吸水率 | 24hr | ASTM D570 | 0.22 | % | |
| 洛氏硬度 | M-Scale | ASTM D785 | 80 | ||
| 機械性能 | 拉伸強度 | Yield | ASTM D638 | 61.7 | MPa |
| 拉伸伸長率 | Yield | ASTM D638 | 55 | % | |
| 彎曲模量 | ASTM D790 | 2620 | MPa | ||
| 彎曲強度 | Yield | ASTM D790 | 90.1 | MPa | |
| 剪切強度 | ASTM D732 | 54.9 | MPa | ||
| Izod缺口沖擊強度 | 3.20mm | ASTM D256 | 58.7 | J/m | |
| 拉伸沖擊強度 | 1.60mm | ASTM D1822 | 118 | kJ/m2 | |
| 電氣性能 | 表面電阻率 | ASTM D257 | 1.0E+16 | ohms | |
| 體積電阻率 | ASTM D257 | 1.0E+14 | ohm·cm | ||
| 電氣強度 | ASTM D149 | 19 | kV/mm | ||
| 介電常數 | 1E+6 Hz | ASTM D150 | 3.70 | ||
| 介質損耗因數 | 1E+6 Hz | ASTM D150 | 0.0070 | ||
| 熱性能 | 熱畸變溫度 | 0.45MPa,未退火 | ASTM D648 | 158 | °C |
| 熱畸變溫度 | 1.8MPa,未退火 | ASTM D648 | 110 | °C | |
| 熔融溫度 | 165 | °C | |||
| 線性熱膨脹系數 | flow | ASTM D696 | 0.000013 | cm/cm/°C | |
| 其它性能 | 阻燃等級 | 0.8mm | UL 94 | HB | |
| 阻燃等級 | 6.4mm | UL 94 | HB | ||
| 無機械性質相對溫度指數 | 0.8mm | UL 746 | 100 | °C | |
| 無機械性質相對溫度指數 | 6.4mm | UL 746 | 100 | °C | |
| 沖擊條件下相對溫度指數 | 0.8mm | UL 746 | 95.0 | °C | |
| 沖擊條件下相對溫度指數 | 6.4mm | UL 746 | 95.0 | °C | |
| 電氣性質相對溫度指數 | 0.8mm | UL 746 | 110 | °C | |
POM/韓國工程塑料/F25-02