BASF PA6 Ultramid B3S物性參數物性表
以下是BASF PA6 Ultramid B3S中英文物性表
|
BASF Ultramid? B3S PA6 (尼龍6-聚酰胺)
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性質
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Density密度
|
1.13 g/cc
|
0.0408 lb/in3
|
ISO 1183
|
|
Water Absorption吸水率
|
9.0 - 10 %
|
9.0 - 10 %
|
ISO 62
|
|
Moisture Absorption at Equilibrium吸濕平衡
|
2.6 - 3.4 %
|
2.6 - 3.4 %
|
23°C/50% R.H.; ISO 62
|
|
Viscosity Measurement粘度
|
145
|
145
|
Viscosity Number; ISO 307
|
|
Linear Mold Shrinkage線性收縮率
|
0.0055 cm/cm
|
0.0055 in/in
|
|
|
Melt Flow熔體流動速率
|
197.75 g/10 min
@Load 11.0 lb, Temperature 527 °F |
ISO 1133
|
|
|
Mechanical Properties力學性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Tensile Strength, Yield屈服拉伸強度
|
90.0 MPa
|
13100 psi
|
50mm/min; ISO 527
|
|
Elongation at Yield屈服伸長率
|
4.0 %
|
4.0 %
|
50mm/min; ISO 527
|
|
Modulus of Elasticity彈性模量
|
3.40 GPa
|
493 ksi
|
ISO 527
|
|
Flexural Modulus彎曲彈性模量
|
3.00 GPa
|
435 ksi
|
ISO 178
|
|
Izod Impact, Notched懸臂梁缺口沖擊強度(ISO)
|
5.00 kJ/m2
|
2.38 ft-lb/in2
|
ISO 180/A
|
|
5.00 kJ/m2
@Temperature -30.0 °C |
2.38 ft-lb/in2
@Temperature -22.0 °F |
ISO 180/A
|
|
|
Charpy Impact Unnotched夏比缺口試樣沖擊
|
25.0 J/cm2
|
119 ft-lb/in2
|
ISO 179/1eU
|
|
20.0 J/cm2
@Temperature -30.0 °C |
95.2 ft-lb/in2
@Temperature -22.0 °F |
ISO 179/1eU
|
|
|
Charpy ImPAct, Notched夏比缺口沖擊
|
0.400 J/cm2
|
1.90 ft-lb/in2
|
ISO 179/1eA
|
|
0.300 J/cm2
@Temperature -30.0 °C |
1.43 ft-lb/in2
@Temperature -22.0 °F |
ISO 179/1eA
|
|
|
Electrical Properties電性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Volume ResiSTivity體積電阻率
|
1.00e+13 ohm-cm
|
1.00e+13 ohm-cm
|
IEC 60093
|
|
Dielectric Constant介電常數
|
3.3
@Frequency 1.00e+6 Hz |
3.3
@Frequency 1.00e+6 Hz |
IEC 60250
|
|
Dissipation Factor耗散因數
|
0.030
@Frequency 1.00e+6 Hz |
0.030
@Frequency 1.00e+6 Hz |
IEC 60250
|
|
Comparative Tracking Index跟蹤指數
|
600 V
|
600 V
|
Test Solution A; IEC 60112
|
|
Thermal Properties熱性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
CTE, linear, Parallel to Flow線性熱膨脹系數
|
0.700 - 1.00 μm/m-°C
@Temperature 23.0 - 80.0 °C |
0.389 - 0.556 μin/in-°F
@Temperature 73.4 - 176 °F |
ISO 11359-1/-2
|
|
Specific Heat Capacity比熱容
|
1.70 J/g-°C
|
0.406 BTU/lb-°F
|
|
|
Thermal Conductivity導熱系數
|
0.330 W/m-K
|
2.29 BTU-in/hr-ft2-°F
|
DIN 52612
|
|
Melting Point熔點
|
220 °C
|
428 °F
|
DIN 53765
|
|
Maximum Service Temperature, Air使用溫度
|
180 °C
|
356 °F
|
|
|
Deflection Temperature at熱變形溫度0.46 MPa (66 psi)
|
180 °C
|
356 °F
|
ISO 75
|
|
Deflection Temperature at熱變形溫度1.8 MPa (264 psi)
|
65.0 °C
|
149 °F
|
ISO 75
|
|
Flammability, UL94阻燃等級
|
V-2
@Thickness >=1.50 mm |
V-2
@Thickness >=0.0591 in |
|
|
Processing Properties加工性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Melt Temperature熔體溫度
|
250 - 270 °C
|
482 - 518 °F
|
Injection-molding/Extrusion
|
|
Mold Temperature模具溫度
|
40.0 - 60.0 °C
|
104 - 140 °F
|
Injection-molding
|